Description:
Carbon fiber fabric is also known as carbon fiber weaving cloth, carbon fiber prepreg, carbon fiber reinforced cloth, carbon fiber tape, carbon fiber sheet (prepreg cloth), etc.
1. The plain weave carbon fiber fabric has a checkered appearance, similar to a chessboard, due to the different light reflections of the fiber bundles in the warp and weft directions.
2. This type of fabric is woven in a regular pattern, where each warp and weft yarn interlaces every other yarn, resulting in many interlacing points. As a result, the fabric is strong, wear-resistant, rigid, and flat.
3. However, its elasticity is low, and its gloss is average. Due to the constant fluctuation of the fiber bundles, there are many fiber bending points, leading to a high elongation rate during stretching.
4. At the same time, due to the interlacing points of adjacent warp and weft yarns, fiber bundles may slide, causing small holes to appear.
1. The twill carbon fiber fabric has a diagonal pattern at a certain angle to the alignment direction of the carbon fiber bundles.
2. This twill pattern has a strong three-dimensional appearance and is used in automotive modification products such as panels, hoods, exhaust pipes, and reinforcements.
3. Two carbon fiber bundles are interwoven at a single weaving position, which leads to the diagonal texture feature of the twill carbon fiber fabric. There are no carbon fiber bundles along the direction of the pattern.
1. This unidirectional carbon fiber fabric is primarily used for structural reinforcement, as most of the time, only force in one direction is needed for such applications.
2. Unlike biaxial fabrics, carbon fibers in unidirectional fabrics are not interwoven, so they are not pulled in the opposite direction. This ensures that the tensile strength is not compromised.
Product Specification:
3K-200g
12K-400g
Item
|
Unit
|
3K -200g
|
12K -400g
|
Plain
|
Twil
|
Plain
|
Twil
|
Average AreaDensity
|
g/m²
|
200±2
|
200±2
|
400±2
|
400±2
|
Average Width
|
mm
|
1000
|
1000
|
1000
|
1000
|
Item
|
I Grade
|
Il Grade
|
Weight
|
200g/m²
|
300g/m²
|
200g/m²
|
300g/m²
|
Thickness
|
0.11lmm
|
0.167mm
|
0.11lmm
|
0.167mm
|
Tensile Strength
|
>3400MPa
|
>3400MPa
|
>3000MPa
|
>3000MPa
|
Tensile Modulus
|
>240GPa
|
>240GPa
|
>210GPa
|
>210GPa
|
Elongation
|
>1.7%
|
>1.7%
|
>1.5%
|
>1.5%
|