Carbon Fiber Laminated Plate

Carbon fiber laminate is a kind of continuous fiber reinforced thermosetting material, prepared by traditional pultrusion molding process, which contains matrix resin and reinforcement material and other components. Resin mainly includes epoxy resin

Description:

Carbon fiber pultruded boards are continuous fiber-reinforced thermoset materials, made using the traditional pultrusion molding process. They contain components such as matrix resin and reinforcement materials. The resins are mainly epoxy, polyurethane, and other types, while the reinforcement materials primarily consist of carbon fibers with different tensile moduli and tensile strengths. These boards are mainly used in the main beam structural components of wind turbine blades.

Product Parameters:

Test ltem
Unit
Value Type
GX60
GX64
GX66

Fiber Volume Fraction
(%)
Mean
60士2
64士2
66士2

Density
g/cm3
Mean
1.56士0.04
1.575士0.04
1.58±0.04

Tg
℃ Mean
≥105
≥105
≥105

0° Tension and Compression Performance
Modulus(GPa)
Mean
≥135
≥142.5
≥147.5

Strength(MPa)
Char.2015
≥1450
≥1600
≥1650

0° Tensile Performance
Modulus(GPa)
Mean
≥140
≥150
≥155

Strain(%)
Char.2015
≥1.0
≥1.0
≥1.0

90° Tensile Performance
Strength(MPa)
Mean
≥40
≥50
≥50

Modulus(GPa)
Mean
≥7.5
≥8
≥8

Strength(MPa)
Char.2015
≥1100
≥1200
≥1250

0°Compression Performance
Modulus(GPa)
Mean
≥130
≥140
≥140

Strain(%)
Char.2015
≥0.8 ≥0.9
≥0.92

90°Compression Performance
Strength(MPa)
Mean
≥142 ≥150
≥152

Modulus(GPa)
Mean
≥8.5
≥8.5
≥9

Strength(MPa)
Char.2015
≥1050
≥1100
≥1200

0° BendingPerformance(4PB)
Modulus(GPa)
Mean
≥130
≥133
≥ 140

Strain(%)
Char.2015
≥0.75
≥0.8
≥0.83

Interlaminar ShearPerformance
Strength(MPa)
Mean
≥56
≥60
≥60

ENQUIRY

Back to list

Hot Products

Home

Carbon Fiber Laminated Plate

Hot Products

Carbon Fiber Prepreg

Carbon Fiber Laminated Plate

Carbon Fiber Precursor

Polyacrylonitrile Carbon Fiber

Carbon Fiber Products

High-Strength Carbon Fiber Production Line

PU production line

Carbon Fiber Composites

Carbon Fiber Composite Production Equipment

Test ltem	Unit	Value Type	GX60	GX64	GX66
Fiber Volume Fraction	(%)	Mean	60士2	64士2	66士2
Density	g/cm3	Mean	1.56士0.04	1.575士0.04	1.58±0.04
Tg	℃	Mean	≥105	≥105	≥105
0° Tension and Compression Performance	Modulus(GPa)	Mean	≥135	≥142.5	≥147.5
	Strength(MPa)	Char.2015	≥1450	≥1600	≥1650
0° Tensile Performance	Modulus(GPa)	Mean	≥140	≥150	≥155
	Strain(%)	Char.2015	≥1.0	≥1.0	≥1.0
90° Tensile Performance	Strength(MPa)	Mean	≥40	≥50	≥50
	Modulus(GPa)	Mean	≥7.5	≥8	≥8
	Strength(MPa)	Char.2015	≥1100	≥1200	≥1250
0°Compression Performance	Modulus(GPa)	Mean	≥130	≥140	≥140
	Strain(%)	Char.2015	≥0.8	≥0.9	≥0.92
90°Compression Performance	Strength(MPa)	Mean	≥142	≥150	≥152
	Modulus(GPa)	Mean	≥8.5	≥8.5	≥9
	Strength(MPa)	Char.2015	≥1050	≥1100	≥1200
0° BendingPerformance(4PB)	Modulus(GPa)	Mean	≥130	≥133	≥ 140
	Strain(%)	Char.2015	≥0.75	≥0.8	≥0.83
Interlaminar ShearPerformance	Strength(MPa)	Mean	≥56	≥60	≥60